Why Need Post Weld Heat Treatment(PWHT)?

Due to the steel pipe transporting gas or liquid need to bear a certain pressure, internal stress produced in the cold rolling process must be eliminated. Welding process, because local overheating will cause the pipe deformation and shrinkage stress, so steel pipe return to heat treatment after welding to eliminate internal stress.

PWHT is based on the hardness of the steel, the thickness of the welding parts, structural rigidity, welding methods and conditions of use. General carbon steel welding performance is good, the welding can be without preheated and heat treatment. But for the high carbon content and high stiffness of the welding parts, it is required to preheat and heat treatment, such as the wall thickness of 30mm carbon steel pipe.

Method of PWHT

The method of PWHT is electric heating. The caterpillar electric heater and linear electric heater should be fixed on the parts which are needed to PWHT; they connect with the automatic controller through cable. And the thermocouple should be fixed on the parts needed to PWHT through the compensating conductor. It connects with the computer automatic controller. Then the controller will work automatically according to the process parameter that is being inputted into the controller.

General rules for PWHT

• On the stress corrosion of the weld, should be carried out post weld heat treatment.

• Prone to delayed crack in steel welding, it should be timely carried out heat treatment after welding. When the heat treatment is not timely, it should be heated to 200℃~300℃ immediately after welding, and the heat preservation and slow cooling, the heating range should be the same as the PWHT.

• After welding heat treatment and before the pressure test, appearance inspection and non-destructive testing should be carried out.

• PWHT qualified parts, should not engage in welding operations, otherwise it should be re-heat treatment.

• Welding inspector should be professional trained and welding heat treatment personnel should be in accordance with the norms and welding work instructions to handle heat treatment.

• When heat treatment is carried out, the temperature should be measured and recorded, the position and quantity of the temperature measuring point should be reasonable, and the temperature measuring instrument should be qualified and effective.